Page 42 - 21-036 APPLITEC catalogue.indb

a e
n
v f
a p
d 1
v c
f z
Q
Application Material [mm] z [m/min] [mm] [mm] [mm] [min ] -1 [mm/min] [cm /min]
3
Nickel-based alloys 3.00 4 35 0.010 5.400 1.800 3715 149 1.4
annealed 4.00 4 35 0.015 7.200 2.400 2785 167 2.9
Rm <1000 N/mm² 5.00 4 35 0.020 9.000 3.000 2230 178 4.8
[Inconel 718] 6.00 4 35 0.020 10.800 3.600 1855 148 5.8
8.00 4 35 0.030 14.400 4.800 1395 167 11.6
10.00 4 35 0.035 18.000 6.000 1115 156 16.9
12.00 4 35 0.045 21.600 7.200 930 167 26.0
16.00 4 35 0.050 28.800 9.600 695 139 38.4
20.00 4 35 0.060 36.000 12.000 555 133 57.5
Nickel-based alloys 3.00 4 25 0.010 5.400 1.800 2655 106 1.0
precipitation hardened 4.00 4 25 0.010 7.200 2.400 1990 80 1.4
Rm > 1000 N/mm² 5.00 4 25 0.015 9.000 3.000 1590 95 2.6
[Inconel 718] 6.00 4 25 0.015 10.800 3.600 1325 80 3.1
8.00 4 25 0.025 14.400 4.800 995 100 6.9
10.00 4 25 0.030 18.000 6.000 795 95 10.3
12.00 4 25 0.035 21.600 7.200 665 93 14.5
16.00 4 25 0.040 28.800 9.600 495 79 21.9
20.00 4 25 0.050 36.000 12.000 400 80 34.6
Manganese steel 3.00 4 40 0.010 5.400 1.800 4245 170 1.7
Mn >5% 4.00 4 40 0.015 7.200 2.400 3185 191 3.3
[1.3964 / Nitronic] 5.00 4 40 0.020 9.000 3.000 2545 204 5.5
[1.3401 / X120Mn12] 6.00 4 40 0.020 10.800 3.600 2120 170 6.6
8.00 4 40 0.030 14.400 4.800 1590 191 13.2
10.00 4 40 0.035 18.000 6.000 1275 179 19.3
12.00 4 40 0.045 21.600 7.200 1060 191 29.7
16.00 4 40 0.050 28.800 9.600 795 159 44.0
20.00 4 40 0.060 36.000 12.000 635 152 65.8
Inox difficult 3.00 4 50 0.015 5.400 1.800 5305 318 3.1
[Cr-Ni-Mo++/1.4529] 4.00 4 50 0.020 7.200 2.400 3980 318 5.5
Heat resistant steel 5.00 4 50 0.030 9.000 3.000 3185 382 10.3
[1.4841] 6.00 4 50 0.035 10.800 3.600 2655 372 14.5
8.00 4 50 0.045 14.400 4.800 1990 358 24.8
10.00 4 50 0.055 18.000 6.000 1590 350 37.8
12.00 4 50 0.065 21.600 7.200 1325 345 53.6
16.00 4 50 0.070 28.800 9.600 995 279 77.0
20.00 4 50 0.085 36.000 12.000 795 270 116.8
PM high-speed steel 3.00 4 80 0.010 5.400 1.800 8490 340 3.3
annealed 4.00 4 80 0.015 7.200 2.400 6365 382 6.6
[Böhler S390] 5.00 4 80 0.020 9.000 3.000 5095 408 11.0
[ASP 2023] 6.00 4 80 0.020 10.800 3.600 4245 340 13.2
8.00 4 80 0.030 14.400 4.800 3185 382 26.4
10.00 4 80 0.035 18.000 6.000 2545 356 38.5
12.00 4 80 0.045 21.600 7.200 2120 382 59.3
16.00 4 80 0.050 28.800 9.600 1590 318 87.9
20.00 4 80 0.060 36.000 12.000 1275 306 132.2
Titanium alloys 3.00 4 70 0.010 5.400 1.800 7425 297 2.9
> 300 HB 4.00 4 70 0.015 7.200 2.400 5570 334 5.8
[Ti6Al4V] 5.00 4 70 0.015 9.000 3.000 4455 267 7.2
6.00 4 70 0.020 10.800 3.600 3715 297 11.6
8.00 4 70 0.025 14.400 4.800 2785 279 19.2
10.00 4 70 0.035 18.000 6.000 2230 312 33.7
12.00 4 70 0.040 21.600 7.200 1855 297 46.2
16.00 4 70 0.045 28.800 9.600 1395 251 69.4
20.00 4 70 0.055 36.000 12.000 1115 245 106.0
Nickel-based alloys 3.00 4 25 0.010 4.200 3.000 2655 106 1.3
annealed 4.00 4 25 0.010 5.600 4.000 1990 80 1.8
Rm <1000 N/mm² 5.00 4 25 0.015 7.000 5.000 1590 95 3.3
[Inconel 718] 6.00 4 25 0.015 8.400 6.000 1325 80 4.0
8.00 4 25 0.025 11.200 8.000 995 100 8.9
10.00 4 25 0.030 14.000 10.000 795 95 13.4
12.00 4 25 0.035 16.800 12.000 665 93 18.8
16.00 4 25 0.040 22.400 16.000 495 79 28.4
20.00 4 25 0.050 28.000 20.000 400 80 44.8
Nickel-based alloys 3.00 4 20 0.005 4.200 3.000 2120 42 0.5
precipitation hardened 4.00 4 20 0.010 5.600 4.000 1590 64 1.4
Rm > 1000 N/mm² 5.00 4 20 0.010 7.000 5.000 1275 51 1.8
[Inconel 718] 6.00 4 20 0.015 8.400 6.000 1060 64 3.2
8.00 4 20 0.020 11.200 8.000 795 64 5.7
10.00 4 20 0.020 14.000 10.000 635 51 7.1
12.00 4 20 0.025 16.800 12.000 530 53 10.7
16.00 4 20 0.030 22.400 16.000 400 48 17.2
20.00 4 20 0.040 28.000 20.000 320 51 28.7