Application Material [mm] z [m/min] [mm] [mm] [mm] [min ] -1 [mm/min] [cm /min]
3
Inox normal 3.00 4 86 0.013 3.750 1.200 9125 475 2.1
[Cr-Ni/1.4301] 4.00 4 86 0.017 5.000 1.600 6845 466 3.7
[Cr-Ni-Mo/1.4571] 5.00 4 72 0.020 6.250 3.250 4585 367 7.5
6.00 4 72 0.024 9.000 3.900 3820 367 12.9
8.00 4 72 0.032 12.000 5.200 2865 367 22.9
10.00 4 72 0.041 15.000 6.500 2290 376 36.6
12.00 4 72 0.049 18.000 7.800 1910 374 52.6
16.00 4 72 0.058 20.000 10.400 1430 332 69.0
20.00 4 72 0.072 25.000 13.000 1145 330 107.2
Inox medium 3.00 4 58 0.013 3.750 1.200 6155 320 1.4
[Cr-Ni-Mo+/1.4539] 4.00 4 58 0.017 5.000 1.600 4615 314 2.5
Duplex steel 5.00 4 53 0.020 6.250 3.250 3375 270 5.5
[17-4 PH] 6.00 4 53 0.024 9.000 3.900 2810 270 9.5
8.00 4 53 0.032 12.000 5.200 2110 270 16.9
10.00 4 53 0.041 15.000 6.500 1685 276 26.9
12.00 4 53 0.049 18.000 7.800 1405 275 38.7
16.00 4 53 0.058 20.000 10.400 1055 245 50.9
20.00 4 53 0.072 25.000 13.000 845 243 79.1
Inox difficult 3.00 4 44 0.012 3.750 1.200 4670 224 1.0
[Cr-Ni-Mo++/1.4529] 4.00 4 44 0.015 5.000 1.600 3500 210 1.7
Heat resistant steel 5.00 4 40 0.018 6.250 3.250 2545 183 3.7
[1.4841] 6.00 4 40 0.022 9.000 3.900 2120 187 6.5
8.00 4 40 0.029 12.000 5.200 1590 184 11.5
10.00 4 40 0.036 15.000 6.500 1275 184 17.9
12.00 4 40 0.043 18.000 7.800 1060 182 25.6
16.00 4 40 0.050 20.000 10.400 795 159 33.1
20.00 4 40 0.061 25.000 13.000 635 155 50.3
Inox martensitic 3.00 4 110 0.017 3.750 1.200 11670 794 3.6
C < 0.3% 4.00 4 110 0.023 5.000 1.600 8755 806 6.4
[Cr/1.4021] 5.00 4 92 0.027 6.250 3.250 5855 632 12.8
6.00 4 92 0.033 9.000 3.900 4880 644 22.6
8.00 4 92 0.043 12.000 5.200 3660 630 39.3
10.00 4 92 0.054 15.000 6.500 2930 633 61.7
12.00 4 92 0.065 18.000 7.800 2440 634 89.1
16.00 4 92 0.079 20.000 10.400 1830 578 120.3
20.00 4 92 0.097 25.000 13.000 1465 568 184.7
Inox normal 3.00 4 63 0.007 2.250 3.000 6685 187 1.3
[Cr-Ni/1.4301] 4.00 4 63 0.009 3.000 4.000 5015 181 2.2
[Cr-Ni-Mo/1.4571] 5.00 4 63 0.013 6.250 5.000 4010 209 6.5
6.00 4 63 0.019 9.000 6.000 3340 254 13.7
8.00 4 63 0.026 12.000 8.000 2505 261 25.0
10.00 4 63 0.032 15.000 10.000 2005 257 38.5
12.00 4 63 0.039 18.000 12.000 1670 261 56.3
16.00 4 63 0.046 20.000 16.000 1255 231 73.9
20.00 4 63 0.058 25.000 20.000 1005 233 116.6
Inox medium 3.00 4 46 0.007 2.250 3.000 4880 137 0.9
[Cr-Ni-Mo+/1.4539] 4.00 4 46 0.009 3.000 4.000 3660 132 1.6
Duplex steel 5.00 4 46 0.013 6.250 5.000 2930 152 4.8
[17-4 PH] 6.00 4 46 0.019 9.000 6.000 2440 185 10.0
8.00 4 46 0.026 12.000 8.000 1830 190 18.3
10.00 4 46 0.032 15.000 10.000 1465 188 28.1
12.00 4 46 0.039 18.000 12.000 1220 190 41.1
16.00 4 46 0.046 20.000 16.000 915 168 53.9
20.00 4 46 0.058 25.000 20.000 730 169 84.7
Inox difficult 3.00 4 35 0.006 2.250 3.000 3715 89 0.6
[Cr-Ni-Mo++/1.4529] 4.00 4 35 0.008 3.000 4.000 2785 89 1.1
Heat resistant steel 5.00 4 35 0.012 6.250 5.000 2230 107 3.3
[1.4841] 6.00 4 35 0.017 9.000 6.000 1855 126 6.8
8.00 4 35 0.023 12.000 8.000 1395 128 12.3
10.00 4 35 0.029 15.000 10.000 1115 129 19.4
12.00 4 35 0.034 18.000 12.000 930 127 27.3
16.00 4 35 0.040 20.000 16.000 695 111 35.6
20.00 4 35 0.049 25.000 20.000 555 109 54.4
Inox martensitic 3.00 4 81 0.007 2.250 3.000 8595 241 1.6
C < 0.3% 4.00 4 81 0.009 3.000 4.000 6445 232 2.8
[Cr/1.4021] 5.00 4 81 0.014 5.000 5.000 5155 289 7.2
6.00 4 81 0.020 7.500 6.000 4295 344 15.5
8.00 4 81 0.026 10.000 8.000 3225 335 26.8
10.00 4 81 0.032 12.500 10.000 2580 330 41.3
12.00 4 81 0.039 15.000 12.000 2150 335 60.4
16.00 4 81 0.047 16.000 16.000 1610 303 77.5
20.00 4 81 0.058 20.000 20.000 1290 299 119.7